MATERIAL
CODES
ssssssssss |
TECHNOLOGICAL
CHARACTERISTICS
|
STANDARD
SINT. PART CODES |
MAIN
APPLICATIONS
|
|||
| DENSITY |
RESISTANCE
TO STRESS
|
STRETCH
|
HARDNESS | |||
|
gr/cm3
|
Rm-N/mm2
|
%
|
HB*
|
|||
|
FSN/A
- 00
|
5,6
- 6,0
|
60
|
-
|
25
|
SINT
A-00
|
IRON-BASED
MATERIALS FOR MAGNETIC USE CONSTRUCTIONS AND SELF-LUBRICATING PARTS
(BUSHES)
|
|
FSN/B
- 00
|
6,0
- 6,4
|
80
|
3
|
30
|
SINT
B-00
|
|
|
FSN/C
- 00
|
6,4
- 6,8
|
130
|
5
|
40
|
SINT
C-00
|
|
|
FSN/D
- 00
|
6,8
- 7,2
|
190
|
10
|
50
|
SINT
D-00
|
|
|
FSN/C
- 10
|
6,4
- 6,8
|
210
|
2
|
55
|
SINT
C-10
|
COPPER-BASED IRON MATERIALS WITH LOW PERCENTANGE OF CARBON, ESPECIALLY SUITABLE FOR LOW MECHANIC-STRESS APPLICATIONS |
|
FSN/D
- 10
|
6,8
- 7,2
|
300
|
-
|
-
|
SINT
D-10
|
|
|
.
|
.
|
|||||
|
.
|
.
|
|||||
|
ANS/C
- 11
|
6,4
- 6,8
|
420
|
2
|
110
|
SINT
C-11
|
COPPER-CARBON
ALLOYED IRON SUITABLE FOR MEDIUM TO HIGH RESISTANCE APPLICATIONS
|
|---|---|---|---|---|---|---|
|
ANS/D
- 11
|
6,8
- 7,2
|
520
|
2
|
130
|
SINT
D-11
|
|
|
ANC/C
- 30
|
6,4
- 6,8
|
300
|
2
|
80
|
SINT
C-30
|
COPPER/CARBON/NICKEL/
MOLYBDENUM ALLOYED IRON, SUITABLE FOR OBTAINING HIGH RESISTANCE METAL PARTS AS WELL AS HEAT-TREATMENT OPERATIONS |
|
ANS/D
- 30
|
6,8
- 7,2
|
500
|
4
|
100
|
SINT
D-30
|
|
|
.
|
.
|
|||||
|
.
|
.
|
|||||
|
INS/C
- 40
|
6,4
- 6,8
|
300
|
2
|
100
|
AISI
316 SINT C-40
|
NSI 316L STAINLESS STEEL SUITABLE TO FOOD AND CHEMICAL INDUSTRY APPLICATIONS |
|
INS/D
- 40
|
6,8
- 7,2
|
400
|
4
|
130
|
AISI
316 SINT D-40
|
|
|
BNS/A
- 50
|
6,4
- 6,8
|
70
|
1
|
20
|
SINT
A-50
|
BRONZE MATERIAL SUITABLE FOR THE PRODUCTIONS OF SELF-LUBRICATING BUSHES AND TECHNICAL PARTS |
|
BNS/B
- 50
|
6,8
- 7,2
|
100
|
2,5
|
30
|
SINT
B-50
|
|
|
.
|
.
|
|||||
|
BNS/A
- 51
|
6,4
- 6,8
|
70
|
1
|
20
|
SINT
A-51
|
BRONZE MATERIALS WITH MOLYBDENUM DISULFIDE AND/OR GRAPHITE TO OBTAIN DRY SELF-LUBRICATING BUSHES FOR BOTH HIGH AND LOW TEMPERATUS |
|
BNS/B
- 51
|
6,8
- 7,2
|
100
|
2,5
|
30
|
SINT
B-51
|
|
*
HARDNESS TEST BY A 2,5 mm DIAMETER AND 62,5 Kg. LOADED SPHERE
Our technicians are fully available for advice on materila choice, (or other) regarding any compound materials not listed in our table.